Self-leveing Compound
Typical Property:
|
Items |
Specifications |
|
|
Flowability (mm) |
Initial flowability |
≥130 |
|
20min flowability |
≥120 |
|
|
Tensile adhesive strength (Mpa) |
≥1.0 |
|
|
Wear resistance (g) |
≤0.50 |
|
|
Dimensional change rate (%) |
-0.15~+0.15 |
|
|
24h compressive strength (Mpa) |
≥4.0 |
|
|
24h anti-bending strength (Mpa) |
≥2.0 |
|
|
28 days compressive strength (Mpa) |
≥13 |
|
|
28 days anti-bending strength (Mpa) |
≥4 |
|
Colorcom Group can tailor make Self-leveing Compounds for multiple uses as per your specific requirements:
Gypsum Self-leveing Compounds, High Strength Gypsum Self-leveling Compound, Cement Based Self-leveling Compound, High Strength Cement Self-leveling Compound, Self-leveling Compound Basecoat Primer are available in Colorcom Group.
Advantages:
It is easy to construct by stirring with water manually or mechanically.
It has good self-leveling and smoothness.
It has high compressive strength and wear-resistance, low shrinkage that is not easy to crack or generate delaminating and hollowing.
It has rapid solidification, smooth surface that can be travelled after 6-8 hours. The plastic floor, carpet and tile can be paved on the surface after 48 hours.
It is environmental and non-toxic product.
Instruction for use:
The substrate must be clean, dry firm and no any residue; Mixed with water before construction by the specified equipment, be sure to strictly thick self-leveling compound: water 25: 7.5~8kg mixed, then use the transport pipe put the mixture into the construction area, a zigzag rake to move to a desired uniform thickness (thickness constructability 5-80mm). Before initial setting, use defoaming roller to exclude air which mixed in before.
Applications:
It is suitable for various raise the ground and leveling;
It is suitable to apply for floor heat pipe backfill project and make the floor leveling.
It is suitable for grand hotel, hall of airport, department stores, meeting room, exhibition center and so on.